CuZn35Pb2Al-C ( CC752S )
| Grad: | CuZn35Pb2Al-C |
| Numru: | CC752S |
| Klassifikazzjoni: | Liga tar-ram-żingu |
| Standard: | EN 1982: 2008 Ram u ligi tar-ram. Ingotti u kkastjar |
| Gradi ekwivalenti: | L-ebda informazzjoni |
Kompożizzjoni kimika % tal-grad CuZn35Pb2Al-C ( CC752S )
| Suffiss -C huwa miżjud mad-denominazzjoni biex jiġi identifikat materjal fil-forma ta 'ikkastjar |
| Fe | Si | Mn | Ni | Al | Cu | Kif | Pb | Sb | Sn | - |
| massimu 0.3 | massimu 0.02 | massimu 0.1 | massimu 0.2 | 0.3 - 0.7 | 61.5 - 64.5 | 0.04 - 0.14 | 1.5 - 2.2 | massimu 0.14 | massimu 0.3 | Zn - bqija |
Proprjetajiet mekkaniċi tal-grad CuZn35Pb2Al-C (CC752S)
| Rm- Saħħa tat-tensjoni (MPa) (GM) | 280 |
| Rp0.20.2% qawwa tal-prova (MPa) (GM) | 120 |
| A- Min. titwil fil-ksur (%) (GM) | 10 |
| Ebusija Brinell (HBW): (GM) | 70 |
Proċess tal-ikkastjar
| GS | Tidwib tar-ramel |
| GM | Ikkastjar tal-moffa permanenti |
| GZ | Casting ċentrifugali |
| GC | Tidwib kontinwu |
| GP | Pressjoni die casting |
Kundizzjonijiet materjali
| R | Kundizzjoni tal-materjal indikata mill-valur minimu tar-rekwiżit tas-saħħa tat-tensjoni għall-prodott b'rekwiżiti obbligatorji ta 'saħħa tat-tensjoni u elongazzjoni |
| H | Kundizzjoni materjali indikata mill-valur minimu tar-rekwiżit ta 'ebusija għall-prodott b'rekwiżiti obbligatorji ta' ebusija |
Proprjetajiet mekkaniċi
| ReH | Minimum yield power / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Saħħa tat-tensjoni / Zugfestigkeit / Reżistenza a la traction |
| A | Titwil minimu / Mindestwert der Bruchdehnung / Allongement minimu |
| J | Talja impatt test / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn35Pb2Al-C (CC752S) Liga tar-ram-żingu |