CuNi30Cr2FeMnSi-C (CC382H)
| Grad: | CuNi30Cr2FeMnSi-C |
| Numru: | CC382H |
| Klassifikazzjoni: | Liga tar-ram-nikil |
| Standard: | EN 1982: 2008 Ram u ligi tar-ram. Ingotti u kkastjar |
| Gradi ekwivalenti: | L-ebda informazzjoni |
Kompożizzjoni kimika % tal-grad CuNi30Cr2FeMnSi-C ( CC382H )
| Suffiss -C huwa miżjud mad-denominazzjoni biex jiġi identifikat materjal fil-forma ta 'kkastjar |
| Fe | C | Si | Mn | Ni | P | S | Cr | Ti | Al | Zr | B | Pb | Se | Mg | Zn | Bi | Te | - |
| 0.5 - 1 | massimu 0.03 | 0.15 - 0.5 | 0.5 - 1 | 29 - 32 | massimu 0.01 | massimu 0.01 | 1.5 - 2 | MAX 0.25 | massimu 0.01 | massimu 0.15 | massimu 0.01 | massimu 0.005 | max 0.005 | massimu 0.01 | massimu 0.2 | massimu 0.002 | massimu 0.005 | Cu - bqija |
Proprjetajiet mekkaniċi tal-grad CuNi30Cr2FeMnSi-C (CC382H)
| Rm- Saħħa tat-tensjoni (MPa) (GS) | 440 |
| Rp0.20.2% qawwa tal-prova (MPa) (GS) | 250 |
| A- Min. titwil fil-ksur (%) (GS) | 18 |
| Ebusija Brinell (HBW): (GS) | 115 |
Proċess tal-ikkastjar
| GS | Tidwib tar-ramel |
| GM | Ikkastjar tal-moffa permanenti |
| GZ | Casting ċentrifugali |
| GC | Tidwib kontinwu |
| GP | Pressjoni die casting |
Kundizzjonijiet materjali
| R | Kundizzjoni tal-materjal indikata mill-valur minimu tar-rekwiżit tas-saħħa tat-tensjoni għall-prodott b'rekwiżiti obbligatorji ta 'saħħa tat-tensjoni u elongazzjoni |
| H | Kundizzjoni materjali indikata mill-valur minimu tar-rekwiżit ta 'ebusija għall-prodott b'rekwiżiti obbligatorji ta' ebusija |
Proprjetajiet mekkaniċi
| ReH | Minimum yield power / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Saħħa tat-tensjoni / Zugfestigkeit / Reżistenza a la traction |
| A | Titwil minimu / Mindestwert der Bruchdehnung / Allongement minimu |
| J | Talja impatt test / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi30Cr2FeMnSi-C (CC382H) Liga tar-ram-nikil |