CuCr1-C ( CC140C )
| Grad: | CuCr1-C |
| Numru: | CC140C |
| Klassifikazzjoni: | Liga tar-ram-kromju |
| Standard: | EN 1982: 2008 Ram u ligi tar-ram. Ingotti u kkastjar |
| Gradi ekwivalenti: | Mur hawn |
Kompożizzjoni kimika % tal-grad CuCr1-C ( CC140C )
| Cr | - |
| 0.4 - 1.2 | Cu + Cr > 99.5; Cu - bqija |
Proprjetajiet mekkaniċi ta' grad CuCr1-C ( CC140C )
| Rm- Saħħa tat-tensjoni (MPa) (GS) jew (GM) | 300 |
| Rp0.20.2% qawwa tal-prova (MPa) (GS) jew (GM) | 200 |
| A- Min. titwil fil-ksur (%) (GS) jew (GM) | 10 |
| Ebusija Brinell (HBW): | 95 |
Proprjetajiet CuCr1-C
| Konduttività elettrika (GS) jew (GM)=MS/m; |
Gradi ekwivalenti ta' grad CuCr1-C ( CC140C )
Twissija! Biss bħala referenza
| UE MT |
il-Ġermanja DIN,WNr |
||
| CuCr1-C |
|
Proċess tal-ikkastjar
| GS | Tidwib tar-ramel |
| GM | Ikkastjar tal-moffa permanenti |
| GZ | Casting ċentrifugali |
| GC | Tidwib kontinwu |
| GP | Pressjoni die casting |
Kundizzjonijiet materjali
| R | Kundizzjoni tal-materjal indikata mill-valur minimu tar-rekwiżit tas-saħħa tat-tensjoni għall-prodott b'rekwiżiti obbligatorji ta 'saħħa tat-tensjoni u elongazzjoni |
| H | Kundizzjoni materjali indikata mill-valur minimu tar-rekwiżit ta 'ebusija għall-prodott b'rekwiżiti obbligatorji ta' ebusija |
Proprjetajiet mekkaniċi
| ReH | Minimum yield power / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Saħħa tat-tensjoni / Zugfestigkeit / Reżistenza a la traction |
| A | Titwil minimu / Mindestwert der Bruchdehnung / Allongement minimu |
| J | Talja impatt test / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuCr1-C ( CC140C ) Liga tar-ram-kromju |